Unless it is a specially customized model, the stainless steel blade barbed rope produced now is generally produced with a 22mm blade length mold, which is what we usually call bto-22 type. It doesn’t have to be the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the specified length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.

Hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. The net color is white and shiny, thick zinc layer, uniform mesh, flat mesh surface, solder joint tension resistance, high corrosion resistance. The surface of the steel wire is usually protected by hot-dip galvanizing, and the thickness of the galvanized protective layer can be made according to the requirements of customers. Hot-dip galvanizing hexagonal net is another kind of twisting mesh corresponding to the galvanizing hexagonal net.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

Maintenance is indispensable in the use of galvanized wire. Large coils of galvanized silk should be coated with oil, fiber core immersion oil, oil is required to protect the fiber core is not rotten, not rust, wire moisture fiber, and from the internal lubrication wire rope. Surface coating so that all wire rope strands in the surface, are evenly coated with a layer of rust-proof lubrication grease, which for friction lifting and mineral water large mine rope, to be coated with grinding and water-resistant black oil grease. Coated with red oil with strong film and good rust resistance, it is required to have a thin oil layer, which is easy to keep clean during operation.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.