Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need to have the condition of many sided, just need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer does not meet the strength requirements in the data, after all, there is no way to make the strength of the product progress, so this is the necessary condition.

Galvanized diamond net to reduce the impact of the project on the environment, protect the slope protection area of the land, maintain the rock can be fully strong, slope protection hook net through artificial planting grass planting, the implementation of green function. Suitable for any complex terrain, at the same time, does not destroy the original landform, the product is mesh distribution, visual interference, convenient for artificial afforestation, conducive to the environment, engineering and environment integration system flexibility.

Now it is more used in the binding of the construction industry. Compared with ordinary iron wire, it is softer and has better luster. Use in daily life does not need to carry out maintenance and maintenance, save a lot of time, but also save the cost of maintenance and maintenance. Annealed wire has good stability, good corrosion resistance, greatly prolonging the service life. More kinds, can be selected according to different uses, making annealing wire device is simple, improve the utilization rate of the device. The material properties of annealed wire can meet different processing requirements.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

The advantages of hexagonal net to do jet hanging net, the first is that the processing speed is fast, the cost is low, and it is very good to roll out when it is open because of the edge. Common specifications: 12 cm x15 cm (11cm x11 cm) 11 cm x15 cm (10 cm x10 cm) 10 cm x12 cm (9 cm x9 cm) 9 cm x13 cm (9 cm x9 cm) 8 cm x10 cm (7 cm x7 cm) common wire: 1.3mm 1.4mm 1.5mm 1.6mm 1.7mm 1.8mm 2.0mm 2.3mm 2.5mm Commonly used materials: galvanized wire hot dip galvanized wire to wire drawn zinc aluminum alloy plastic coated wire stainless steel wire.

Galvanized iron wire is very common in practical application, some people think that galvanized iron wire will not rust, in fact, it is not. Metal corrosion is caused by the chemical or electrochemical action of the surrounding medium. According to different media, it is divided into atmospheric corrosion, soil corrosion, seawater corrosion, bacterial corrosion and so on. Atmospheric corrosion is more common, because metal products in the process of processing, transportation and storage, when in contact with the atmosphere, there are always atmospheric corrosion conditions.