In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

2, the production and installation is simple and fast, the use of patented friction connection or special connection accessories for installation, greatly improve the installation efficiency.

Blade thorn rope because the volume is relatively large so thorn rope factory is used to packaging treatment.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

The bonding and anchoring function between cold wire drawing and cold rolled ribbed steel bar and concrete is outstanding. Therefore, when used in components, the phenomenon of cracking of component anchorage area and damage caused by steel wire slip is fundamentally eliminated, and the load-bearing ability and anti-cracking ability of component end are improved. In reinforced concrete structure, the crack width is smaller than that of circular steel bar or even that of hot rolled thread bar.

Spring wire shall have high tensile strength, elastic limit, endurance and fatigue strength, and be resistant to shock and oscillation. The objectives of strength and endurance, especially the prevention of alteration cracks, are key to the consumption of spring steel wires. The inner and outer quality of wire rod directly affect the function of steel wire.

Compared with other galvanizing processes, galvanized steel wire has low cleaning requirements before plating. However, under the current trend of increasing the quality level of galvanized layer, some pollutants brought into the plating tank are obviously harmful. Because cleaning galvanized coating wastes a lot of time and reduces production, it is very important to properly clean and effectively rinse the substrate before electroplating.

This oxide film has greater elasticity and lubricity, does not affect the accuracy of parts. Therefore, the parts of precision instruments and optical instruments, spring steel, thin steel sheet, fine steel wire and so on are commonly bluing treatment. The commonly used galvanizing treatment of large roll galvanized wire is equivalent to forming a protective layer on the surface of the iron wire. The commonly used methods are hot dip galvanizing, hot spray plating, vacuum plating and so on. Different methods have corresponding characteristics.