Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.

When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well. Galvanized wire, also known as hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

Unless the stainless steel blade barbed rope produced now is a specially customized model, it is generally produced with a tool length of 22mm, which is what we usually call bto-22 type. It is not necessarily such a specification from 11mm to 65mm there are specifications. Unless the customer insists on customizing the specified length, the barbed rope manufacturer produces the bto-22 stainless steel blade barbed rope.

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Wire factory reminds you in the purchase of galvanized wire, should be stored in dry, ventilated conditions, do not contain corrosive gases, do not mix with organic volatile gas produced paint, plastic and other substances in a good environment. If possible, we can add reliable inner packaging for galvanized parts, and put desiccant. If the zinc layer of white spots and long hair, can only be removed by mechanical methods, and then normal passivation, or completely washed off the zinc layer after re-plating.

1. The diameter of the raw material and the thickness of the diameter are directly affected;