Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

The technical term “galvanized” means that metal has been specially treated with zinc. Essentially, the wire is covered with a very thin layer of zinc. It is this thin layer of zinc that gives galvanized wire its many properties. Galvanizing can be done by dipping wire into a pool of zinc or by electroplating.

The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.

The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

Hexagonal twist flower network is divided into heavy hexagonal network and small hexagonal network two categories. Both are made of steel wire braided with various materials, the difference is that the former uses thicker steel wire, and the latter uses finer steel wire braided.

Since galvanized iron wire will rust, we need to pay attention in the process of storage and use, try to store in a dry and ventilated environment, in the process of use to avoid damaging the surface of galvanized iron wire, we can slow down the time of galvanized iron wire rust.

When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.