For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

1, no paint and maintenance, long new not old, exempt you from maintenance fatigue and trouble, the lowest comprehensive cost. Stainless steel wire mesh can be used as poultry cage, egg basket, channel fence, drain tank, porch guardrail, anti rat net, mechanical protective cover, livestock and plant fence, grid frame, etc.

Zinc is a silver-white metal, brittle at room temperature, soluble in acid and alkali, known as amphoteric metal. Pure zinc is more stable in dry air, and small in humid air or water containing carbon dioxide and oxygen. A thin film layer of basic zinc carbonate will be formed on the surface, which can delay the corrosion rate of zinc layer. The corrosion resistance of galvanized layer in aqueous solution of acid, alkali and sodium chloride is relatively strong. It is also not resistant to corrosion in atmospheres containing carbon dioxide and hydrogen sulfide and in Marine atmospheres; In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded.

There is no need to carry out daily maintenance and maintenance when in use, which can not only save a lot of time, but also reduce the cost, but also has good stability, strong corrosion resistance, greatly extend the service life. According to the different technology is divided into different types, can be selected according to their own needs, has better flexibility and elasticity. The main function of annealing wire is to control its hardness, when the annealing wire is made of steel wire.

The application of electric welding net is more widely, at present it has replaced the use of other parts of the wire mesh, the cost of electric welding net is lower, the production speed is very fast, so it is very popular. Welding net galvanized before the need for processing is recrystallization annealing, because the welding net must maintain a no oxide and no other impurities of pure iron active surface, if you can not keep its surface clean will lead to a bad galvanizing effect, galvanized layer and iron material is not closely combined, so this step is necessary.

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip galvanizing and cooling. Galvanized iron wire has resistance and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, wire mesh, highway guardrail, commodity packaging and ordinary civilian and other fields.

Traditional wire mesh is crisscross woven into the wire, with the development of the economy, the rapid rise of all walks of life, the use of traditional wire mesh limitations gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven up the net wire once the mesh is too large net surface will become soft.

The application of electric welding mesh is more widely, at present, it has replaced the use of other parts of the screen, the cost of electric welding mesh is low, the production speed is very fast, so it is very popular. The treatment required before galvanized welding mesh is recrystallization annealing, because the welding mesh must maintain an oxide and no other impurities of pure iron active surface, if you can’t keep its surface clean will lead to poor galvanized effect, galvanized layer and iron material is not tightly combined, so this step is necessary.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.