- 3. The transport, storage and use of the binder of galvanized wire mesh should adopt safety and fire prevention methods according to the relevant regulations, so as to be safer.
Post time: 19-04-23When using these two products, it is obvious that there is a gap between them. By pulling or bending the wire, it is often difficult to restore the original, for example, if the same place is repeatedly bent, it will be found that it has broken, and the cold drawing wire will not. Cold drawing wire compared with iron wire, its hardness, tensile resistance, bending ability is greatly enhanced, suitable for building materials.
When the barbed rope is used, it is calculated according to the length, while when purchasing the barbed rope, it is calculated according to the weight of the barbed rope, which causes the confusion of users’ difficulty in counting the quantity of purchase. Therefore, it is necessary to understand clearly that there are less meters per kilogram of the barbed rope. How much does a barbed rope weigh in a meter? These two problems, the purchase of barbed rope becomes very simple.
Post time: 20-09-22- Annealed wire is a kind of soft iron wire made of low carbon steel by cold drawing, heating, constant temperature and heat preservation. The composition of the wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet is rolled into 6.5mm thick steel bar, that is, the wire rod, and then it is put into the wire drawing device to draw the wire of different diameter, and gradually reduce the aperture of the drawing disk, cooling, annealing, plating and other processing technology to make a variety of different specifications of the wire.
Steel wire mesh by its own unique advantages in construction occupation, reinforcement anti-crack occupation is indispensable reinforcement anti-crack data, high product error is small, mesh mesh uniform, welding firm, strong acceptance, not easy to deformation, steel wire mesh in different fields have different called, in bridge engineering construction people call it soft reinforcement.
Most people in addition to pay attention to the price of barbed rope, many people for hot-dip galvanized barbed rope or cold galvanized barbed rope will have questions, in fact, these two products, the price difference is not very big, so how to choose hot-dip galvanized barbed rope and electric galvanized barbed rope?
The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.
Stainless steel wire is characterized by good corrosion, in chemical plants or pharmaceutical industry can often be used to stainless steel wire, suitable for acid, alkali environment. Aluminum alloy wire is characterized by high temperature, can adhere to the high temperature of more than 100 degrees Celsius does not fade, and has good corrosion, patience is also very good. It can be used for device manufacturing in construction industry.
For example, Przewalskopeles is a first-class protected animal in China. At present, as long as there are several other przewalskopeles populations around Qinghai Lake in China, according to incomplete statistics, there are only about 1,000 of them left. Stainless steel barbed wire fence net is commonly used in grassland pastoral area of Qinghai Lake, with a height of 1.5 meters.
- 4, the material requirements of the silk: change wire braid, electric galvanized wire braid, hot galvanized wire braid, first braid after hot plating.
The tensile strength of cold drawn spring steel wire is slightly higher than that of oil tempered steel wire. The large specification of cold drawn steel wire elastic force is too large, winding the spring is very difficult, so the cold drawn spring steel wire application specification is generally less than 8.0mm, oil quenching tempered steel wire application specification is generally less than 13.0mm. In fact, the diameter of 13.0mm spring is used to light tension spring steel wire, cold drawing wound made into shape and then quenched and tempered. Steel wire with diameter above 15.0mm is mostly made by heating winding process.
- The optional height of this type of wire mesh is 1 meter, 1.2 meters, 1.5 meters, 1.8 meters, 2 meters. The latter three are the most commonly used, too low to achieve the fence protection effect. The mesh size is divided into 3 cm and 6 cm, and the vast majority of 6 cm is used.
Post time: 29-09-22The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.
- 1, we should pay attention to the welding mesh moisture-proof: if it is just the general outdoor air humidity, do not bother. If the weather is foggy, use dry cotton cloth to wipe the bead on the welding mesh; If it rains, you should dry the water when the rain stops. Try to maintain and prolong the life of the welding mesh.
Post time: 11-10-22
Post time: 15-03-23We must have a certain understanding of the hexagonal network, we are the beautiful shape of the hexagonal network, more than the appearance of the hexagonal network is very beautiful, in fact, the practical value of survival is very high. To introduce the relevant information should be very clearly know the highway guardrail net, hexagonal wire netting in all kinds of fence netting, in the value of the high-speed on the road more MaoJian, it not only be used in all kinds of road, in a sports ball games venue and try our best to take care of landslides, also has reached very matter effectiveness.
- Three is to do a good job of galvanized silk product production site clean and tidy, in accordance with the scientific method of operation to operate the production, the operator should wear the required dress. If it is hot dip galvanized wire products, we must do a good job of passivation treatment, will be able to effectively prevent discoloration, prolong the method of discoloration, can solve the problem of discoloration.
Post time: 15-06-223. Acid activation acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts, without excessive corrosion on the matrix.
Post time: 05-05-23
Post time: 09-03-23