Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.

With the improvement of living standards and the reduction of family size, keeping pets is becoming a way of life for many people. According to statistics, the number of pet dogs has reached more than 100 million, and the trend is increasing rapidly every year. Beijing alone had more than 900,000 licensed dogs in 2010, according to a survey, and the number of pet cats is also very large.

The whole country is cooling down on a massive scale. People suddenly feel that winter is coming. In much of the north, the collection of central heating and heating has also begun. People who do not have central heating or do not want to use traditional heating choose air heating. As heating equipment enters the peak season, building network sales are also gradually increasing.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

Because of the corrosion resistance of zinc layer, can be applied to all kinds of environment, it is also very convenient to use, has been a more popular hardware products. Galvanized iron wire should pay special attention to the acyl wash, to slowly into the container, to prevent acid sputtering on the body, at the same time prohibit the water into, so it is easy to let the acid out, to learn to handle lightly, stacking should also be firm and neat. It can be widely used in construction, handicrafts and other daily civilian applications.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

Stainless steel barbed rope is often used in various engineering projects because of its good anticorrosion ability, but it is difficult to be accepted by ordinary families because of its high price. So what material of barbed rope has better anticorrosion ability?

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.