Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Galvanized barbed wire (barbed wire) is made of galvanized barbed wire twisted on the main wire, so as to play a protective and isolation role. Among them twist weave way is divided into single twist weave and double twist weave. Construction methods include direct installation and spiral insertion.

In order to make the zinc content of steel wire stable in the future, and maintain its uniformity, as far as possible to reduce the zinc content, and effectively reduce zinc consumption to the actual work, the following measures are proposed by the wire factory:

The size of the galvanized layer of galvanized iron wire is related to the anti-corrosion ability and application effect of galvanized wire. The thickness of the galvanized layer of the general standard galvanized wire products should be tested after the product is formed. There are three specific test methods. Weighing method and cross section microscopy method are destructive experimental methods, and magnetic method is a relatively rigorous non-destructive method, but the measurement steps and requirements are relatively high, so they are rarely used in specific applications. The first two methods are intuitive and common methods.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

Stainless steel is short for rust acid steel, air, steam, water and other weak corrosion medium or stainless steel is called stainless steel; And the chemical corrosion resistance medium (acid, alkali, salt and other chemical etching) corrosion of steel called acid steel.

Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

In the purchase of barbed rope should be customer demand, so the amount of galvanized is different, then the two kinds of barbed rope and what is the difference, some customers need high zinc blade barbed rope, but high zinc blade barbed rope price to ordinary galvanized barbed rope price is more than 1000 yuan per ton, the two kinds of barbed rope products, the former is used in many aspects, such as the military, the government’s barbed rope, The latter is more for civilian use.