For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

The bonding and anchoring function between cold wire drawing and cold rolled ribbed steel bar and concrete is outstanding. Therefore, when used in components, the phenomenon of cracking of component anchorage area and damage caused by steel wire slip is fundamentally eliminated, and the load-bearing ability and anti-cracking ability of component end are improved. In reinforced concrete structure, the crack width is smaller than that of circular steel bar or even that of hot rolled thread bar.

Titanium and titanium alloy with light weight, high strength, corrosion resistance and many other characteristics, titanium and its alloy not only in aviation, aerospace industry has a very important application, and has begun to chemical, petroleum, light industry, power generation, metallurgy and many other civil industrial sectors are widely used. However, titanium and titanium alloy are smaller than steel in terms of hardness and strength. The shortcomings of titanium alloy wire made of titanium alloy in terms of hardness limit its breadth and depth of application.

4. Keep the rinsing water clean after wire pickling, which is an important link to reduce zinc consumption. The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate.

Many customers are in great need of galvanized barbed rope when they decide to purchase it, and the barbed rope specification determines the length of the later installation.

Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

Galvanized wire A stable layer of zinc is coated on the outside of the wire, which is used to protect the wire and make the wire service life longer. When producing galvanized wire, the wire is pickled. Pickling is to use some acid mist or acid to wash off some oxides on the surface of iron, that is, rust, and some other corrosive substances, to achieve the purpose of cleaning iron, so that zinc will fall off when galvanizing.