Domestic iron wire factory has been able to consume wire rope, radial low steel wire, umbrella steel wire, spring steel wire, bicycle saddle spring steel wire and other products. In the 1980s, hot – plated low carbon steel wire, fan net cover steel wire, carbon structure steel wire, bed steel wire and so on were also published. The elongation of wire is increased after annealing. Make the product more soft and increase the scope of application of the wire.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.

The bonding and anchoring function between cold wire drawing and cold rolled ribbed steel bar and concrete is outstanding. Therefore, when used in components, the phenomenon of cracking of component anchorage area and damage caused by steel wire slip is fundamentally eliminated, and the load-bearing ability and anti-cracking ability of component end are improved. In reinforced concrete structure, the crack width is smaller than that of circular steel bar or even that of hot rolled thread bar.

As we all know, the mechanism of resistance to atmospheric corrosion of zinc includes mechanical protection and electrochemical protection. Under the condition of atmospheric corrosion, there are ZnO, Zn(OH)2 and basic zinc carbonate protective film on the surface of zinc layer, which to a certain extent slows the corrosion of zinc. When this protective film (also known as white rust) is damaged, a new film will be formed.

Now large roll galvanized wire in our life the use of more and more, to galvanized wire products bring a great market, galvanized wire products are more and more types. The surface coating of good quality galvanized wire is continuous and smooth. When the plating parts are installed and combined, there can be no flow hanging, slag or drop remaining, and no surface defects such as iron exposure. Good quality galvanized wire, coating must be uniform, roughly uniform in copper sulfate solution soaking five times without exposing iron. And with hammering test does not bulge, do not fall off. This is a good galvanized wire should have characteristics.

Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.