The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.

Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, which is characterized by beautiful, lightweight, folding, easy to store. The surface treatment of pet cage is generally: cold galvanized, hot galvanized, spray, dip, chromium plating, nickel plating and other methods.

The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

The technical term “galvanizing” means that the metal has been specially treated with zinc. Essentially, it’s wire covered with a very thin layer of zinc. It is because of this thin layer of zinc that galvanized wire has many characteristics. Zinc can be galvanized by dipping the wire into a zinc bath or by electroplating.

The stainless steel barbed rope is made of stainless steel material after processing. The barbed rope has the characteristics of corrosion resistance and aging resistance. So why is the price of stainless steel barbed rope more expensive than ordinary barbed rope? Where do you want to go?

Electrode application range is wide, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding. (1) Welding between low carbon steel, low alloy steel, medium carbon steel, alloy steel and other metal materials or dissimilar metal materials can be achieved. The weld has good comprehensive mechanical properties, and the tensile strength can reach more than 400MPa. ⑵ Can realize the welding of large plate, steel frame, plate – tube, rod – rod, tube – tube and other profiles. ⑶, can realize docking, Angle, lap, T joint and other joint forms of welding. ⑷ mainly suitable for flat welding.(5) it can surfacing the parts of wear failure, so as to obtain the surface surfacing layer with melting depth, smooth surface and excellent performance. ⑹ It can be realized that no bevel 1 ~ 6mm thick metal sheet single-side welding double-side molding.