Hexagonal net structure can be used for slope support, excavation, rock face net mine support form, slope vegetation (green color), railway road isolation block, it can be made into a cage, cushion, used for rivers, flood dam and seawall erosion protection and storage reservoir, river closed cage. Driving and guiding rivers, river flood disaster is a major water and river erosion of destruction, resulting in flooding, resulting in a great deal of loss of property by the amount of soil and water dissipation. Because of this, in dealing with these problems, the application of the habitat grid structure becomes a solution plan, which has the potential to protect the bank forever.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Due to the influence of production process or other factors, the zinc layer of galvanized wire products will be different to a certain extent, especially ordinary galvanized can not reach the beauty of electric galvanized, ordinary galvanized wire zinc layer is mainly for anticorrosion and corrosion prevention. Large volume galvanized wire products refers to the use of high quality low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes, some galvanized wire products are made of iron wire galvanized.

The barbed wire factory will store the blade barbed wire inventory in the appropriate place, because it understands the product characteristics.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.