Large coil galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling process and other processing. Galvanized wire is divided into hot galvanized wire and cold galvanized wire. Galvanized wire in the process of smelting there are a lot of need to pay more attention to the place, galvanized wire products in the manufacturing process will experience a lot of process, of which the following galvanized wire annealing is a very important step, this step to the nature of galvanized wire has brought a lot of help.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

(2) Packing and binding galvanized shaft wire order notes: ① the galvanized iron wire shall not be damaged when the tightening. (2) Stop the use of more than two strands of galvanized iron wire around the operation method. ③ The diameter of galvanized wire for pulling should not be less than 4mm, and the diameter of galvanized wire for binding should not be less than 2.6mm. (4) Galvanized iron wire shall not be used as waist hoop down reinforcement, usually not used as a whole binding. Warehouse galvanized wire is mainly used to block and distinguish the function of the area, warehouse galvanized wire is one of the primary use of galvanized wire, warehouse galvanized wire primary layout features are as follows: layout: Column mesh frame, column to choose square steel pipe, galvanized wire frame is also a small square pipe as the data, column and mesh frame corresponding direction are welded connecting ear piece (flat iron), column and mesh frame through the connection of the ear piece bolt fixed, column bottom welding plate, column bottom plate through expansion bolts and fixed on the ground.

1. Adjust electroplating process parameters

3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.