Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

For mountainous or hilly areas where the ground is more undulating set up stakes. You need to set a stake at the beginning and the end, and then determine the position. In the middle of the ups and downs, to increase the stakes according to the complexity of the ups and downs of the terrain, we need to be able to see 3 stakes at the same time, so that the installation is. It’s a straight line.

(1) The application method of packaging and binding galvanized shaft wire ordering: ① the pulling position on the goods should be reasonably selected. When used to avoid horizontal movement of goods, the pulling position should be as low as possible; When used to avoid overturning the goods, the pulling position can be appropriately high. ② The use of galvanized iron wire [1] pull reinforcement methods mainly include: figure eight, inverted figure eight, cross, zigzag or reverse zigzag and so on. Various pull methods can be used alone, but also two or more than two kinds of use. The pull should be as symmetrical as possible. (3) When pulling reinforcement, the single or double strands of galvanized iron wire will reciprocate around the goods and vehicles between the two tying nodes, and should be pulled tight galvanized iron wire so that the tightness of each strand is as common as possible, and some of the remaining cross around its own rope rod, and the rest of the tail toward the car.