4. Keep the rinsing water clean after wire pickling, which is an important link to reduce zinc consumption. The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate.

Industrial rust prevention method: coated with asphalt, iron roof, coated with asphalt, you can prevent rust. Metal coating: Some metal surface will form a dense oxide film, can be coated on the surface of the metal composed of this metal screen. Such as: galvanized iron, tinplate plating, bicycle underwire and some medical equipment are coated with chromium and nickel.

Some raw materials in the production of unstable processing, the wire itself will exist burr, surface small pits and other local defects. Galvanized steel in galvanized, generally should pay attention to the galvanized layer protection time of galvanized wire, and the thickness of galvanized layer has a great relationship. Generally speaking, when the main gas is relatively dry and used indoors, the galvanized layer thickness of galvanized wires is only 6-12μm, and under relatively harsh conditions, the galvanized layer thickness of galvanized wires needs 20μm, and can be predicted to reach 50μm.

Wire factory reminds you in the purchase of galvanized wire, should be stored in dry, ventilated conditions, do not contain corrosive gases, do not mix with organic volatile gas produced paint, plastic and other substances in a good environment. If possible, we can add reliable inner packaging for galvanized parts, and put desiccant. If the zinc layer of white spots and long hair, can only be removed by mechanical methods, and then normal passivation, or completely washed off the zinc layer after re-plating.

Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.

Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.