Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.

No matter how good the quality of hot-dip galvanized barbed rope is, it is only attached to the surface of the wire with galvanized layer, and with the cause of chemical reaction, the zinc layer on the surface will gradually lose its effect because of oxidation reaction, which is more prominent in the humid area of the environment. And because, after all, the wire will rust, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

Hexagonal mesh is also known as twisting mesh, thermal insulation net, soft edge net. It is made of single – layer mesh. Its mesh, mesh wire, galvanized and PVC film properties and the same as the cage. This product can be different shapes and sizes of the block stone into the alloy net to form a flexible whole, can be lifted, car, shipping to the designated place, the alloy net connected to each other into a larger whole, construction throwing convenient, fast, good economic performance.