Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

The distance between the adjacent two thorn rope installation do not know whether you have noticed? Careful observation can find that its spacing is not the same, the thorn rope factory for customer consultation when asking the installation height of the reason.

Hexagon mesh weight calculation method is: hexagon mesh weight calculation method: wire.× wire.× base x length x width ÷2=kg base: 1/2′=2.151′=1.273/4′=1.65/8′=1.875/4′=1.091′x1/2′ : 3′=0.4 warp.× Warp.×2x length x width ÷8×3=kg

Now it is mainly 12 or 14 galvanized barbed rope. Although they are calculated according to the price per ton, the calculation is different when it comes to every meter, because the thickness of the silk is not the same, which causes the problem that one galvanized barbed rope of equal weight is longer and the other is longer. Customers must have detailed communication with the barbed rope factory before purchasing to avoid such problems.

When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.

Low and medium carbon steel wire is used as raw material, with good surface gloss, uniform zinc layer, strong adhesion, corrosion resistance and so on. Available: diameter 1.60mm-4mm (16#-33#) cold plating wire; Diameter 6.40mm-0.81mm(8#-21#) black iron wire, changed wire. It is mainly used in communication equipment, medical equipment, weaving net, brush, steel cable, filter, high-pressure pipe, construction, crafts and other industries.