In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Cold wire drawing is a kind of cold processing of metal, that is, we often say reinforcement. Cold drawing process is not messy, cold drawing price based on the quality of cold drawing dividends of different levels, cold drawing production is also a variety of different procedures. The main factor affecting the strength of cold drawing wire is raw materials, which are closely related to the raw materials, strength and diameter of raw materials, and the better the quality of cold drawing wire, the more messy the production process.

Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.

Unless the stainless steel blade barbed rope produced now is a specially customized model, it is generally produced with a tool length of 22mm, which is what we usually call bto-22 type. It is not necessarily such a specification from 11mm to 65mm there are specifications. Unless the customer insists on customizing the specified length, the barbed rope manufacturer produces the bto-22 stainless steel blade barbed rope.

After annealing, the extension rate of galvanized wire is increased, making the product more soft and increasing the scope of application of galvanized wire. After electric galvanized hot galvanized, electroplated copper and other widely used screen production. Building reinforcement binding with galvanized wire mesh braided with the first after plating, plating and other methods, after treatment of galvanized wire mesh or steel wire mesh, has good corrosion resistance, oxidation resistance characteristics, can be used in construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries reinforcement, protection and heat preservation.