The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.

In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

Because there are many large livestock in pasture, and because of the large cost of development and easy to be destroyed by livestock, galvanized barbed rope is the best choice for enclosure. Pasture installation thorn rope is necessary,  wire mesh factory to introduce the role of pasture installation thorn rope。

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

No matter how good the quality of hot-dip galvanized barbed rope is, it is only attached to the surface of the wire with galvanized layer, and with the cause of chemical reaction, the zinc layer on the surface will gradually lose its effect because of oxidation reaction, which is more prominent in the humid area of the environment. And because, after all, the wire will rust, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

Galvanized barbed wire as a safety protection of the metal wall, the galvanized barbed wire device also need to be protected for a long time? And how to protect it? Maintenance and protection of galvanized barbed rope. First, we can start from two aspects. One is about the protection of galvanized barbed rope posts.

Advantages: The cost of hot dip galvanized rust prevention is lower than that of other paint coating. In suburban environment, the standard hot-dip galvanized rust prevention thickness can adhere to more than 50 years without repair. In urban or offshore areas, the standard hot-dip galvanized rust protection layer can last 20 years without repair. Galvanized layer and steel is a metallurgical connection, into a part of the steel surface, so the durability of the coating is more reliable.