Because the coating obtained is thicker, hot-dip galvanizing has very good protective function than electric galvanizing, so it is an important maintenance coating for iron and steel parts in strict working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding and other occupations. In the field of agriculture, such as pesticide irrigation, greenhouse and construction industry such as water and gas transportation, wire casing, scaffolding, Bridges, highway guardrail and other aspects, it has been widely used in these years.

Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.

Customers do not need to worry about the impact of the production cycle when ordering products from the thorn rope factory, because the overall treatment is now focused on the waste gas, so the production of thorn rope should be said to have the least impact. Customers ordering products in the thorn rope factory can rest assured that the delivery time this piece, can provide customers with goods on time. If the production cycle is not affected, then customers will be more assured of the thorn rope factory.

The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

Barbed rope is to use iron wire, through winding machine, through a variety of weaving technology, wound in the main line (stranded) made of isolation protection net. There are three ways to twist the barbed rope, as detailed below.

There is still some demand for galvanized barbed rope by daily residents, but often the quantity is not particularly much. If the barbed rope factory delivers goods, then the extra freight may be higher than the price of the customer to buy the barbed rope in the market. The thorn rope factory sells to customers who buy in large quantities. There is a lot of demand for it, and it also hopes to find a manufacturer to purchase.

The silver powder is actually a mixture of aluminum powder and polymer after painting the film, the film is brittle, easy to appear adhesion problems, and corrosion resistance is also slightly poor. Galvanizing refers to the surface of metal, alloy or other materials coated with a layer of zinc to play the role of beautiful, rust prevention and other surface treatment technology. Zinc dissolves easily in acids and also in bases, so it’s an amphoteric metal. Zinc changes little in dry air.