Generally speaking, there are three kinds of anti-corrosion and anti-rust skills: surface dipping, spraying and surface galvanized, these three ways are to strengthen their anticorrosion ability and resist natural risks, extend their service life. Today we want to talk about the difference between dip plastic hook and galvanized hook.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

Materials of qualified quality should be kept marked for reference when used. In order to remove the surface film, surface inclusion and other defects on the surface of the large roll galvanized wire on the surface of the sedimentary layer to the local surface, it can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. The presence of small homogeneous particles of large denier in the tank can stabilize the foam layer, but the accumulation of too many solid particles can cause explosion.

High quality galvanized wire in general, the zinc layer attached to the surface of the wire is relatively thick, so when we buy galvanized wire, as long as we look at the thickness of the zinc layer machine, we can generally judge whether the quality of galvanized wire is high quality.

Large rolls of galvanized wire in oxygen violently extinguished, spark, and sodium block, magnesium strip in oxygen extinguished, no spark phenomenon. This phenomenon is determined by the composition of galvanized wire. The galvanized wire used in the experiment is pig iron or steel wire, pig iron and steel are iron and carbon alloy, containing iron and carbon two elements of complex material. Carbon in galvanized wire will produce carbon dioxide when extinguished, solid into gas, volume will shrink rapidly.