The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

The type of barbed rope is mainly reflected in the specification of the wire diameter, the thicker the diameter of the barbed rope produced is shorter, at the same time, the price is cheaper, mainly because the production efficiency is relatively high, because the price of the barbed rope is calculated according to the weight when it is sold. On the contrary, the finer the diameter of the wire, the longer the price is higher.

Temporary rust prevention is to prepare for the completion of the mission of the protective layer to be removed. The methods include: cajoling corrosion inhibitors, coating antirust oil, peeling molecular compound plastics, drying air, vacuuming, etc. Change the internal structure of the metal: new chromium, nickel and other alloy elements made of stainless steel, but the alloy is not much, expensive, difficult to produce widespread application.

In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Welding net is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal pens, flower pens, window bars, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative items.

4. Keep the rinsing water clean after wire pickling, which is an important link to reduce zinc consumption. The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate.