Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.

Steel mesh jinsu appearance treatment: polyethylene thermoplastic powder coatings is also called polyethylene powder coating, is the high pressure polyethylene (LDPE) as the basic material, adding a variety of function additives, colors, its antiseptic powder coating manufacturing processes, jinsu coating layer has the function of chemical, shock, circuitous, acid, salt fog corrosion, decorate a function and has good appearance.

Large roll galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Large roll galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics.

Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it should also be reasonable for post-treatment to avoid affecting its use effect. Of course, when the black iron wire is galvanized, the thickness of the galvanized layer should be ensured, so that the possibility of rust can be reduced. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.