Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.

In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

Now many industrial products will be made of stainless steel wire rope material. In order to identify the fake and inferior stainless steel, certain measures and methods can be taken. But many customers do not know what way to identify, listed the following identification methods for you.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

Large coil galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling process and other processing. Galvanized wire is divided into hot galvanized wire and cold galvanized wire. Galvanized wire in the process of smelting there are a lot of need to pay more attention to the place, galvanized wire products in the manufacturing process will experience a lot of process, of which the following galvanized wire annealing is a very important step, this step to the nature of galvanized wire has brought a lot of help.