If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.

Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.

The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.

The price of galvanized iron wire performance is the key to win, galvanized wire only with good performance, in order to win the market, in order to obtain customer praise. In galvanized wire, the main function of carbon in increasing hardness, less is less easy to rust, the main function of chromium is acid and alkali resistance; Nickel’s main function is high temperature resistance, acid and alkali resistance and conductive use; The main function of iron is magnetic conductivity; The main functions of titanium are low density, high hardness and strong corrosion resistance. The main function of copper is magnetic and electrical conductivity. Different chemical components have different functions, which together form the characteristics of galvanized wire.