Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

Every time galvanized wire production enters the peak season of the industry, the road leading to the factory will see from time to time transport wire and container vehicles, as well as galvanized bright wire short-distance transport trucks, driving the labor utilization rate in the surrounding countryside, solving the employment problem of most people. Galvanized wire is divided into hot dip galvanized wire and cold galvanized wire difference: hot dip galvanized is in the heated melting zinc liquid dip plating, production speed is fast, the coating is thick but not uniform. Dark color, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanizing in outdoor environment can be maintained for decades.

Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Galvanized electric welding mesh refers to the mesh made of zinc alloy material, because of its high strength, high hardness, beautiful appearance, bright color and other advantages, become used in residential communities. Traditional electric welding mesh using iron bars, aluminum alloy materials, need to use welding and other technology, and the texture is soft, easy to rust, single color.

Compared with other galvanizing processes, galvanized steel wire has low cleaning requirements before plating. However, under the current trend of increasing the quality level of galvanized layer, some pollutants brought into the plating tank are obviously harmful. Because cleaning galvanized coating wastes a lot of time and reduces production, it is very important to properly clean and effectively rinse the substrate before electroplating.

5, after the light plating should be carried out light treatment.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.