Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

The common weight standard of galvanized barbed rope is 25kg per coil, and the length of each coil varies from 220-250 meters according to the specifications of the barbed rope. And of course we all know that the heavier the disc the longer it is. But there is one point that is worth our attention, that is, the hollow inside the general larger disk is relatively small, and the hollow inside the lighter galvanized thorn rope is relatively large. The purpose of this is to reduce the number of bending of the thorn rope and make it easier and more beautiful when installing, on the other hand, it looks larger in appearance.

The steel mesh is also called longitudinal reinforcement and transverse reinforcement. The longitudinal reinforcement and transverse reinforcement are spaced at right angles to each other, and all the crossing points are welded together. It has the characteristics of crack – proof, small error and good quality. Steel mesh is mainly used in coal mine roadway, concrete pavement, bridge deck, airport runway and buildings. So, what are the advantages of mesh?

Under any application environment, users hope that the welding mesh has better strength, as long as it has improved in strength, it will make better use of the demand, but to make the strength of this product improve, also need to have many conditions, to see what kind of data manufacturers have in production, the strength of the product is the strength of the data, But a manufacturer does not meet the strength requirements in the data, and naturally, it cannot make the strength of the product improve after all, so this is the condition.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.