The quality of hot-dip galvanized barbed wire is only in the surface of the wire attached to the galvanized layer, and with the reason of the chemical reaction, the surface of the zinc layer will gradually lose its role because of the oxidation reaction, this situation is more prominent in humid areas. And because after all, the steel wire will rust, so the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.

Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging.

Wire mesh first welding after galvanized is through the end of welding and then cold this company to produce wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot dip galvanized. First galvanized after welding is to change wire mesh, after the end of welding can see the solder joint; The two processes are different in price. The cost of plating after welding is low, the appearance is smooth, and the cost of plating after welding is high, and it is not easy to rust.

Open pit coal mine due to poor air quality, a variety of harmful heavy metals are also more, so the corrosion strength of barbed rope products is particularly large, when using galvanized barbed rope must choose hot plating or plastic coated galvanized barbed rope, although the price is slightly higher, but in the long term development is more appropriate. Besides, when the barbed rope is installed near the coal mine, the pile foundation should be fixed to prevent the barbed rope from falling down due to soil erosion, thus losing the protective effect.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.