Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.

The height of the shield should not be less than two meters. The length of the shield should be the width of the journey and the extension 10 meters away. The vertical load of the handrail on the bridge is 1.2KM/m, and the horizontal external load is 2.5KM/m, both of which should be calculated separately. Galvanized hook mesh is attributed to a hook mesh, it is the selection of galvanized wire, hot dip galvanized wire as raw materials, woven through the hook mesh crimping truncated.

Stainless steel barbed rope service life is, of course, the longer the better. But do you know how to extend the service life of stainless steel barbed rope?

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging.

As we all know, even if it is the same kind of steel wire, because of the steel making process, wire drawing process and equipment are not the same, so the quality of steel wire production is not the same. Due to the different mechanical properties of steel wire itself, flattening process and equipment, the width and elongation of steel wire in the flattening process have different effects. Therefore, in the selection of wire diameter, the following three factors should be considered:

Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements. Galvanized iron wire equipment is specially used for the plating of iron. Generally speaking, the stability of zinc is much higher than that of iron, and it will not rust in the daily water vapor or damp place.

4. Keep the rinse water clean after pickling the steel wire

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.