Polyvinyl Butyral Resin (PVB) is a solvent Resin synthesized by the acetal reaction of Polyvinyl Alcohol (PVA) and butyraldehyde in contact with coal.

Because Pvb Resin itself contains a lot of hydroxyl groups, it can bridge with some thermosetting resins to improve the properties of chemicals and film hardness.

Because PVB resin has the above excellent characteristics, it is widely used in adhesive safety glass intermediate film of automobile and building, rust cutting primer, baking paint, wood paint, printing ink, adhesive of electronic ceramics and printed circuit board, adhesive between metal and metal, between metal and plastic, modifier of hot-melt adhesive, iron dimension waterproof processing of textile, etc. A variety of new industrial applications are also continuously developed and applied.

The general characteristics of PVB are as follows:

The appearance of polyvinyl butyral (PVB) resin is white spherical porous particles or powder, and its specific gravity is 1:1; However, the filling density is only 0.20 ~ 0.35g/ml.

Thermal properties

The glass transfer temperature (TG) of polyvinyl butyral (PVB) resin ranges from 50 ℃ of low degree of recombination to 90 ℃ of high degree of recombination; The glass transfer temperature can also be adjusted by adding an appropriate amount of Plasticizer to reduce it below 10 ℃.

Mechanical properties

The coating of polyvinyl butyral (PVB) resin has good water resistance, water resistance and oil resistance (it is resistant to aliphatic, mineral, animal and vegetable oils, but not to sesame oil). PVB is widely used in printing inks and coatings because it contains high hydroxyl groups and has good dispersibility to pigments.

In addition, its chemical structure contains both hydrophobic acetal and acetic ACID groups and hydrophilic hydroxyl groups, so PVB has good adhesion to glass, metal, plastic, leather and wood.

Chemical reaction

Any chemical that can react with secondary alcohol will also react with PVB. Therefore, in many applications of PVB, it is often used with thermosetting resin to bridge and harden with the hydroxyl group of PVB, so as to achieve the characteristics of chemical resistance, solvent resistance and water resistance.

Of course, films with different characteristics (such as hardness, toughness, impact resistance, etc.) can be prepared according to different types of thermosetting resin and different mixing ratio with PVB.

Safety properties

Polyvinyl butyral (PVB) is dissolved into 12 ~ 14% solution with ethanol and made into film. It is used for printing paper film of ceramic (or enamel) products. The fired ceramic (or enamel) patterns have bright color and smooth texture. The flower paper is characterized by convenient use, low cost, smaller than the original glue, greatly reducing the decal process and high color burning rate. At present, most porcelain factories in China have formed relatively formal production lines for standardized production. Therefore, the demand for PVB in the ceramic (or enamel) flower paper industry is increasing.

Application field of polyvinyl butyral -- electronic adhesive

Polyvinyl butyral contains hydroxyl, vinyl acetate and butyraldehyde, which has high bonding properties. Phenolic Resin was added into PVB ethanol solution to make adhesive, which can be used for a long time at 120 ℃. The product has strong adhesion to metal, wood, leather, glass, fiber and ceramics; FRP can be manufactured to replace non-ferrous metals such as steel, aluminum and copper; The adhesive made by adding this product and curing agent into epoxy resin is often used for bonding and assembly of electronic instrument components, bonding between metal and porous materials, emergency repair, etc. it can also be used in the field of electronic ceramics. In the development of ceramic integrated electronic circuits, this product with medium viscosity and low hydroxyl is used as ceramic powder adhesive to increase the primary strength of ceramics.

Application field of polyvinyl butyral -- copper foil adhesive

Polyvinyl butyral (PVB) and phenolic resin cooperate to produce copper foil adhesive, which is used in the production of copper clad laminate. It has good peel strength and tin welding temperature resistance, and is widely used in various fields.

Application field of polyvinyl butyral - self adhesive enamelled wire paint

Polyvinyl butyral is the main raw material of self-adhesive enamelled wire paint. After the enameled wire is wound and formed in the electrodes of motors, electrical appliances and instruments, as long as it is heated for several minutes at a certain temperature or treated with appropriate solvent, the coils can be bonded together by themselves without impregnation and drying.