The use of electric welding mesh is very wide, can be used in many places. In the field of construction, especially the wall crack, has played a very important role, the traditional construction, is to put on mortar directly onto the wall, after such a long time, will appear fall off and fracture phenomenon, in order to prevent the occurrence of this phenomenon, must use welded wire mesh before rendering, welded wire mesh is fixed to the wall, above the plastering construction, Can ensure that the wall level for a long time, not easy to crack phenomenon.

Barbed rope factory not only provides the sales of blade barbed rope, including the subsequent construction is also contracted, and the construction price is particularly different.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.

(1) The application method of packaging and binding galvanized shaft wire ordering: ① the pulling position on the goods should be reasonably selected. When used to avoid horizontal movement of goods, the pulling position should be as low as possible; When used to avoid overturning the goods, the pulling position can be appropriately high. ② The use of galvanized iron wire [1] pull reinforcement methods mainly include: figure eight, inverted figure eight, cross, zigzag or reverse zigzag and so on. Various pull methods can be used alone, but also two or more than two kinds of use. The pull should be as symmetrical as possible. (3) When pulling reinforcement, the single or double strands of galvanized iron wire will reciprocate around the goods and vehicles between the two tying nodes, and should be pulled tight galvanized iron wire so that the tightness of each strand is as common as possible, and some of the remaining cross around its own rope rod, and the rest of the tail toward the car.

Construction welding net work wall insulation project using galvanized welding network in wall insulation and rust engineering project plays a necessary role, wall painting batch putty network is divided into two kinds: this is galvanized welding network; Another is to change the wire drawing wire welding mesh, according to the provisions of the region, construction enterprises to carry out effective material selection. Construction welded wire mesh new mink cage new mink cage grommet see more 1 inch, from silk in 2 mm up and down, management method is simple and easy, a mesh surface bright and clean and is not easy to scratch mink, galvanized welded wire online zinc quantity proportion, it is not easy to rust, new mink cage up more convenient, mink settled in natural environment more comfortable, the price also is higher than before the same specifications of the mink cage competitive many, But the overall character is not harmed at all, it is stronger.

The quality of hot-dip galvanized barbed wire is only in the surface of the wire attached to the galvanized layer, and with the reason of the chemical reaction, the surface of the zinc layer will gradually lose its role because of the oxidation reaction, this situation is more prominent in humid areas. And because after all, the steel wire will rust, so the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.