Remind you to buy galvanized iron wire, should be stored in dry, good ventilation conditions, do not contain corrosive gases, do not mix with the production of organic volatile gas paint, plastic and other substances in a good environment. If conditions, for galvanized parts to increase reliable inner packaging, and put desiccant. If the zinc layer white spots and hair, only mechanical removal, and then normal passivation, or thoroughly washed off the zinc layer after re-plating.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

Cold plating is a physical treatment method, the zinc is simple and uneven, the amount of zinc is also less than in the corrosion and rust prevention and chemical disposal of hot plating; The amount of hot zinc plating is relatively thick, the surface of the disposal is flat on average, and it is not easy to fall off. A layer of alloy composed of zinc and metal has very strong oxidation ability, and there is a layer of pure zinc on the outside of this layer of alloy, which is why hot plating is thicker and stronger than cold plating. Under the condition of high degree of natural recovery, galvanized hook net can play a very good maintenance effect on the environment, it is not afraid of wind and rain, it is the battle machine in the hook net, much stronger than the dip plastic hook net.

The external environment has a great influence on the storage of cold drawn wire. Especially during the rainy season, special attention should be paid to the air humidity of workshops and warehouses. It is recommended to use moisture test paper with a value between 8 and 10. If the PH value is high, attention should be paid to the corrosion of the internal cold drawing wire. Cold drawing wire in normal environment storage for two years no problem, cold drawing wire will not be corroded. However, it is necessary to place the coil gently during the handling process to avoid the winding position leading to the cable is not smooth.

Large volume galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 grams/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, silk screen preparation, highway guardrail, product packaging and daily civil and other fields. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire).

Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

The application of electric welding mesh is more widely, at present, it has replaced the use of other parts of the screen, the cost of electric welding mesh is low, the production speed is very fast, so it is very popular. The treatment required before galvanized welding mesh is recrystallization annealing, because the welding mesh must maintain an oxide and no other impurities of pure iron active surface, if you can’t keep its surface clean will lead to poor galvanized effect, galvanized layer and iron material is not tightly combined, so this step is necessary.