1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

What’s the difference between cold galvanized wire and hot galvanized wire? It is mainly different production process. Cold galvanized iron wire, also known as electric galvanized iron wire, is the use of electrolytic galvanizing process, and hot galvanized iron wire is the use of hot penetration galvanizing process. Compared with the two, hot dip galvanized iron wire thick coating, high zinc content, has stronger anti-corrosion and anti-rust effect. Similarly, the price is also higher, cold galvanized iron wire and hot galvanized iron wire which good? Mainly for the use of scenarios and requirements to choose appropriate galvanized iron wire, appropriate is better.

Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

In order to improve the corrosion resistance of steel pipe, the general steel pipe is galvanized. Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.

Stainless steel barbed rope is often used in various engineering projects because of its good anticorrosion ability, but it is difficult to be accepted by ordinary families because of its high price. So what material of barbed rope has better anticorrosion ability?

In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Compared with the traditional braided and twisted barbed rope, the price of raw materials is relatively high because of the relatively complex technology.