The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

There are many categories of large coils of galvanized wire, and different categories can be applied to different scenarios. Galvanized iron wire common application is the application of the construction industry, one is the use of binding wire, whether it is the binding of scaffolding or reinforcement, need galvanized iron wire to carry out, the common specifications are 22 and 24 wire, common length of 30cm, 35cm, 40cm, 45cm, 50cm. There is also 20kg or 50kg a bundle of 18, 16, 14, 12, 10 galvanized coil wire.

If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.

Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

To many people, a dog cage looks like a prison, but for dogs who have been raised on cage training, it is their home and shelter. A cage should be a comfortable place. Never put a dog in a cage for no reason. They will see it as punishment. (Why do many dogs fail to adapt to their owners’ commands, because whether the paparazzi can come out or not, it is also seen as a punishment.

The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

6, the use of special formula and special UV absorbent, no fading, no yellowing, no peeling, no cracking, no foaming, no moth, the use cycle can be more than 30 years.

The technical term “galvanized” means that metal has been specially treated with zinc. Essentially, the wire is covered with a very thin layer of zinc. It is this thin layer of zinc that gives galvanized wire its many properties. Galvanizing can be done by dipping wire into a pool of zinc or by electroplating. Are you familiar with galvanized wire mesh? Do you know what to pay attention to in the process of use?

Cold galvanizing, also called electric galvanizing, is the use of electrolytic equipment to remove oil, pickling, after the pipe fitting into the composition of zinc salt solution, and connected to the negative electrode of the electrolytic equipment. Wire factory on the opposite side of the pipe fittings placed zinc plate, connected to the positive electrode of the electrolytic equipment is connected to the power supply, the use of current from the positive electrode to the negative electrode will deposit a layer of zinc on the pipe fittings, cold plating pipe fittings is first processed after galvanized.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.