Now many hardware manufacturers produce iron wire, and iron wire is very easy to rust, if you need to use in outdoor or humid places, generally customers will require the use of galvanized iron wire equipment to give the wire a layer of zinc, the thickness can be determined according to user requirements. Galvanized iron wire equipment is specially used for the plating of iron. Generally speaking, the stability of zinc is much higher than that of iron, and it will not rust in the daily water vapor or damp place.

Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.

The main raw material of blade barbed rope is galvanized wire and galvanized sheet, because the price of galvanized sheet is more expensive than galvanized wire, so it is directly reflected in the price of the sales of blade barbed rope. There is also the difference in processing technology also led to the difference in the price of the blade thorn rope. The traditional barbed rope is mechanically twisted, which uses less labor and has high production efficiency. But the blade is after two mechanical processing in the manual processing operation before the appearance. So whether from the labor force or from the production efficiency also said there is a large gap. These factors lead to the price of blade thorn rope is more expensive the main factor.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

With the opening of metro in large and medium-sized cities, as well as the vigorous promotion of subway service in network tools, those who have been accustomed to the subway as a daily means of transportation and urban traffic. These citizens, who love the subway, rely on it and enjoy its speed, often like to call themselves the U-pin price. Is widely used in industry, agriculture, farming, construction, transportation and other welded wire mesh is used in the field of high quality low carbon wire line of welding and become, then after cold, hot dip plating, PVC plastic coated surface passivation, such as plasticizing processing, production of metal mesh with smooth surface, uniform mesh, solder joint is firm, stability, corrosion resistance, good corrosion resistance characteristics.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

The production process of stainless steel blade piercing rope is basically similar to that of galvanized blade piercing rope, and the blade size is usually determined according to the mold.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.