A pet carrier can be used as an indoor or outdoor pet house. The dog cage is equipped with a fixed food basin and water fountain, and the foot plate pet cage rubber pad has bayonets on four sides to be splintered. It can be spliced, cut and disassembled according to the size of the cage. It is convenient and easy to clean. It can solve the problem of pinching the feet of the puppies in the ordinary cage and prevent the puppies from causing adverse reactions in the development. The dividers are breathable and comfortable, and can be used as heat shields for pets in summer. A puppy with small feet, no feet, no pinching.

Because of its light weight, strength is relatively large has gradually begun to replace the original column. At the same time, due to the relatively uniform specifications, the barbed rope installation is also more beautiful. The direct spacing of the barbed rope is relatively fixed, which can effectively prevent crossing. At the same time, the mesh at the bottom is relatively dense, while the mesh at the top is relatively loose, which can save resources.

Large roll galvanized wire is simply galvanized iron wire, usually used wire is often visible, because iron is very easy to be corroded and rusted, so it is necessary to put a layer of other not easy to rust metal plating in the outer layer, to achieve the effect of corrosion resistance and rust resistance, the effect of zinc can do more. Therefore, many customers often require hardware factories to produce galvanized iron wire, which requires the use of galvanized iron wire equipment.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

The steel mesh is also called longitudinal reinforcement and transverse reinforcement. The longitudinal reinforcement and transverse reinforcement are spaced at right angles to each other, and all the crossing points are welded together. It has the characteristics of crack – proof, small error and good quality. Steel mesh is mainly used in coal mine roadway, concrete pavement, bridge deck, airport runway and buildings. So, what are the advantages of mesh?

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.