There are many important details that need to be paid special attention to during the production of barbed rope or blade barbed rope by the barbed rope factory. If any improper, it will cause unnecessary losses.

Since galvanized iron wire will rust, we need to pay attention in the process of storage and use, try to store in a dry and ventilated environment, in the process of use to avoid damaging the surface of galvanized iron wire, we can slow down the time of galvanized iron wire rust.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Large volume galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire has good toughness and elasticity, the amount of zinc can reach 300 grams/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Widely used in construction, handicrafts, silk screen preparation, highway guardrail, product packaging and daily civil and other fields. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire).

Some raw materials in the production of unstable processing, the wire itself will exist burr, surface small pits and other local defects. Galvanized steel in galvanized, generally should pay attention to the galvanized layer protection time of galvanized wire, and the thickness of galvanized layer has a great relationship. Generally speaking, when the main gas is relatively dry and used indoors, the galvanized layer thickness of galvanized wires is only 6-12μm, and under relatively harsh conditions, the galvanized layer thickness of galvanized wires needs 20μm, and can be predicted to reach 50μm.

The technical term “galvanized” means that metal has been specially treated with zinc. Essentially, the wire is covered with a very thin layer of zinc. It is this thin layer of zinc that gives galvanized wire its many properties. Galvanizing can be done by dipping wire into a pool of zinc or by electroplating.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.