5, according to the wire diameter thickness to adjust zinc dipping time

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

Traditional barbed wire is woven into wire, with the development of the economy, the rapid rise of all walks of life, the limitations of the use of traditional barbed wire gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven mesh wire once the mesh over the surface of the net will become soft. We also have the solutions: 1, rolling the straight wire into a wavy shape, but still not enough to feed chickens with mesh can only stretch out the chicken beak can not feed! 2, is electric welding mesh, with the current to the longitude and latitude of the wire spot welding together, mesh do more than most is not restricted.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

The amount of zinc on the surface of high zinc barbed rope is about 5 times that of general zinc barbed rope, thus greatly prolonging the time of rust resistance. In the appearance of the two products are silver white and metal texture is better, for the distinction between the two products is more difficult to distinguish if it is a layman, but for long-term work of professionals can be separated from the two at a glance.