The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

Low and medium carbon steel wire is used as raw material, with good surface gloss, uniform zinc layer, strong adhesion, corrosion resistance and so on. Available: diameter 1.60mm-4mm (16#-33#) cold plating wire; Diameter 6.40mm-0.81mm(8#-21#) black iron wire, changed wire. It is mainly used in communication equipment, medical equipment, weaving net, brush, steel cable, filter, high-pressure pipe, construction, crafts and other industries.

Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries, in the agricultural field such as pesticide irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Take 20cm galvanized wire for acid fog experiment, check the zinc content of galvanized wire through the balance to see whether it meets the zinc layer standard required by customers, ensure that the metal wire achieves the role of rust and corrosion prevention, and meet the service life required by customers. Galvanized iron wires must be packed in good condition, bound neatly and orderly, and bound inward to prevent scratches during transportation. The inspection standard of galvanized iron wire also includes the tensile test, which is decided according to the material of the galvanized wire order ordered by the customer, and it needs to be tested by comparing the raw material list.