Infrared analysis showed that the characteristics bands for the bare nanoparticles are still exhibited in the vitamins@P25TiO₂NPs spectra, such as a wide peak in 450–1028 cm⁻¹ related to the stretching vibration of Ti-O-Ti and other peaks in 1630 cm⁻¹ and 3400 cm⁻¹, which represent the surface OH groups stretching. The IR spectrum of vitaminB2@P25TiO₂NPs showed signs of binding between compounds. The OH bending peak (1634 cm⁻¹) corresponding to bare nanoparticles disappeared, and the NH₂ bending band characteristic of vitamin B2 appeared (1650 cm⁻¹). The IR spectrum of vitaminC@P25TiO₂NPs also showed signs of successful functionalization. Bands at 1075 cm⁻¹; 1120 cm⁻¹; 1141 cm⁻¹ were observed, which are originated by CO-C vibrations present in the vitamin C. The intense band at 1672 cm⁻¹ is attributed to the C = O stretching in the lactone ring while the peak at 1026 cm⁻¹ is ascribed to the stretching vibration Ti-O-C. Wide bands at 3880–3600 cm⁻¹ are related to stretching vibration OH groups, but those disappear in the modified nanoparticles spectrum. These observations confirm the interactions between the P25TiO₂NPs and the vitamins [35].

The vitaminC@P25TiO₂NPs, on the other hand, were obtained through an optimized method based on Mallakpour et al. [27]. Initially, 0.02 g of P25TiO₂NPs were dispersed in 1 mL of ultrapure water and stirred in a Vortex. Next, 100 μL of HCl (0.01 M) were added (pH 2) to 100 uL of P25TiO₂NPs to avoid gel formation. Then, 100 μL of vitamin C dissolved in ultra-pure water (5.0 × 10⁻³ M) solution were added to the mixture and was ultrasonicated for 30 min. Finally, vitamin C was added in excess to gain a beige-orange color suspension, and the ultrasonication continued for another 30 min. The pellet obtained after centrifuging the suspension for 10 min at 4500 rpm was resuspended in ultrapure water, centrifuged again, and then lyophilized.

One of the key advantages of using anatase titanium dioxide in coatings is its superior UV resistance. This makes it ideal for outdoor applications where coatings are exposed to sunlight and other environmental factors that can degrade the finish over time. Anatase titanium dioxide helps to protect the underlying surface from UV rays, preventing fading and deterioration.